Effects of V content on the microstructure and mechanical properties of Nb31Ti37-xZr26Al6Vx refractory medium-entropy alloys

R. Huangb J. Tanc W. Lib Q. Dongc C.J. Lib X.M. Qinc S.F. Guod Y.P. Lua

  • School of Materials Science and Engineering, Dalian University of Technology, Dalian, 116024, China

  • School of Materials Science and Engineering, Kunming University of Science and Technology, Kunming, 650093, China

  • College of Materials Science and Engineering, Chongqing University, Chongqing, 400044, China

  • Faculty of Materials and Energy, Southwest University, Chongqing, 400715, China

Abstract

Most refractory complex concentrated alloys (CCAs) exhibit limited plasticity and high density, which greatly limits their large-scale applications. To address these issues, a series of Nb31Ti37-xZr26Al6Vx(x = 3, 5, 7, 9, and 11 at. %) refractory medium-entropy alloys (RMEAs) were designed and prepared in this work with the help of phase diagram calculation software. The synergistic effects of V and Ti on the microstructure, mechanical properties, and strengthening mechanisms of Nb31Ti37-xZr26Al6Vx RMEAs are investigated in detail. Compared with the reported CCAs with limited plasticity and high density, our alloys with a single BCC structure offer excellent compressive plasticity greater than 50% at room temperature and a lower density less than 6.4 g/cm3. Alloys have higher yield strength at room temperature with the increasing content of V. The high yield strength of alloys primarily originates from the inherent yield strength of the alloy's components and the solution strengthening resulting from the lattice distortion. The alloys studied in this work provide evidence that the high-strength RMEAs with excellent plasticity can be obtained through careful composition design.




https://blog.sciencenet.cn/blog-4773-1321826.html

上一篇:Nonisothermal crystallization behavior of micron-sized
下一篇:Effect of W on the thermal stability, mechanical properties
收藏 IP: 222.178.202.*| 热度|

1 杨正瓴

该博文允许注册用户评论 请点击登录 评论 (0 个评论)

数据加载中...

Archiver|手机版|科学网 ( 京ICP备07017567号-12 )

GMT+8, 2024-12-24 11:47

Powered by ScienceNet.cn

Copyright © 2007- 中国科学报社

返回顶部