Ternary Co-W-B bulk metallic glasses with ultrahigh strength

已有 1423 次阅读 2020-6-9 16:23 |个人分类:非晶前沿|系统分类:论文交流

Ternary Co-W-B bulk metallic glasses with ultrahigh strength

Limin Lai Kailu Ding Tianhao Liu Yanxia Chen Shengfeng Guo

  • Scholl of Materials and Energy, Southwest University, Chongqing 400715, China

Abstract

In this work, a family of ternary Co100-x-yWxBy (at.%, x=15~30, y=11~19) bulk metallic glasses (BMGs) with near-recorded ultrahigh strength up to 6 GPa was successfully developed. With extremely high tungsten content, the Co-W-B BMGs show very high glass transition temperature of 850-975 K and high density of 11.13-12.43 g/cm3, which are much higher than most of Co-based BMGs previously reported. Moreover, the glassy alloys exhibit a good glass-forming ability with critical diameter of 2 mm in diameter and a wide supercooled liquid region of over 80 K. Furthermore, these BMGs possess ultrahigh strength of 5.5–6 GPa, high Young's modulus of 243.6-273.1 GPa, high specific strength of ~ 500 Nm/g and obvious plastic strain of 0.5-2.6 %, respectively. The novel ternary Co-based BMGs with outstanding mechanical properties and less components are promising as structural materials and model system for theoretical research.


https://doi.org/10.1016/j.jnoncrysol.2020.120194




http://blog.sciencenet.cn/blog-4773-1237145.html

上一篇:中国铝产业的发展现状及展望
下一篇:Effect of free-end torsion on microstructure and mechanical

0

该博文允许注册用户评论 请点击登录 评论 (0 个评论)

数据加载中...

Archiver|手机版|科学网 ( 京ICP备07017567号-12 )

GMT+8, 2021-10-24 11:16

Powered by ScienceNet.cn

Copyright © 2007- 中国科学报社

返回顶部